Thermoelastic properties and c’-solvus temperatures of single-crystal Ni-base superalloys(7)
Release time: 2021-03-22
The Einstein model usually provides a good approximation of heat capacity and thermal expansion at temperatures above about hE/2. In the case of the superalloys investigated in this work, the Einsteinapproach describes well the observe...
Views
Thermoelastic properties and c’-solvus temperatures of single-crystal Ni-base superalloys(6)
Release time: 2021-03-19
Calculated and measured phase compositions: The compositions of the c- and c-phase ( & cc and cc&) in the four investigated alloys were measured with 3D APT (ERBO 1) [36] and with TEM-EDX (ERBO 15 and derivatives) [32]. The exper...
Views
Thermoelastic properties and c’-solvus temperatures of single-crystal Ni-base superalloys(5)
Release time: 2021-03-18
Results Elastic properties: The elastic stiffnesses of pseudosingle-crystal ERBO/15 and its variants as obtained by the RUS method at room temperature are presented in Table 4. For comparison, data for ERBO/1 from the literature [41] hav...
Views
Thermoelastic properties and c’-solvus temperatures of single-crystal Ni-base superalloys(4)
Release time: 2021-03-15
According to Demtro¨der et al. [41], the large-scale heterogeneities associated with the castmicrostructure (dendrites and interdendritic regions) can influence the resonances with wave lengths of the order of the dendrite spacing. Foll...
Views
Thermoelastic properties and c’-solvus temperatures of single-crystal Ni-base superalloys(3)
Release time: 2021-03-12
Figure 2 presents SEM micrographs of the eight material states, which were considered in the present work. The four as-cast materials states are presented in the upper row of Fig. 2. The fully heat-treated material states after the secon...
Views
Thermoelastic properties and c’-solvus temperatures of single-crystal Ni-base superalloys(2)
Release time: 2021-03-11
The present work investigates how much large (ERBO/1 vs. ERBO/15) and small (three ERBO/15 variants) variations in alloy composition affect their thermoelastic properties. First objective: The comparison of two different alloys (large va...
Views
Thermoelastic properties and c’-solvus temperatures of single-crystal Ni-base superalloys(1)
Release time: 2021-03-10
ABSTRACTThe present work shows that thermal expansion experiments can be used to measurethe c-solvus temperatures of four Ni-base single-crystal superalloys (SX), one with Re &and three Re-free variants. In the case of CMSX-4, experi...
Views
fine equiaxed microstructures in additively manufactured Nickel alloy 718 (4)
Release time: 2021-05-07
According to Hunts steady state model , the CET mainly depends on three factors: the thermal gradient G, the solid/liquid interface velocity V and the number of potent nucleants ahead of the columnar front. Such analysis has been perform...
Views
fine equiaxed microstructures in additively manufactured Nickel alloy 718 (3)
Release time: 2021-05-07
Several aggregates of nearest-neighbour grains having multiple-twin orientation relationships (OR) have been found in the equiaxed zone. Figure 2(a) shows an assembly of grains in twinning orientation relationships, obtained from ...
Views
fine equiaxed microstructures in additively manufactured Nickel alloy 718 (2)
Release time: 2021-05-07
Samples of 150 x 27 x 7 mm3of Nickel alloy 718 alloy were manufactured using a common commercially available Nickel alloy 718 wire for welding applications (1.2 mm diameter). A Precitec CoaxPrinter laser head was used with a continuous l...
Views
fine equiaxed microstructures in additively manufactured Nickel alloy 718 (1)
Release time: 2021-05-07
Nickel alloy 718 is a heat-treatment hardenable alloy that has been used for decades in aeronautical, aerospace andnuclear industries due to its excellent fatigue and corrosion resistance up to 650◦C. Hence, this alloy has been usedearl...
Views
PROPERTIES OF NI BASE SUPERALLOYS
Release time: 2021-03-03
Creep rupture strength It is well indicated in that the creep-rupture-life/ gamma-prime-fraction plots are different for each series of alloys but every series is likely to have a maximum in the vicinity or more than 75 vol%. This means ...